| Grade |
Density
g/cm3 |
Bending Strength
Mpa |
Compression Strength
Mpa |
Shore Hardness
HS |
Porosity
% |
Thermal Expansion
10-6/ °C |
Maximum operating temperature °C |
|
M108F |
1.65 |
60 |
200 |
80 |
2.0 |
5.0 |
200 |
| M118F |
1.75 |
65 |
210 |
85 |
2.0 |
5.0 |
200 |
| M108K |
1.65 |
60 |
200 |
80 |
2.0 |
5.0 |
200 |
| M118K |
1.75 |
65 |
210 |
85 |
2.0 |
5.0 |
200 |
| M188F |
1.76 |
75 |
220 |
85 |
2.0 |
5.0 |
200 |
| M188K |
1.76 |
75 |
220 |
85 |
2.0 |
5.0 |
200 |
| M104D |
2.9 |
90 |
250 |
85 |
2.0 |
5.5 |
350 |
| M118D |
2.40 |
95 |
250 |
85 |
2.0 |
5.5 |
400 |
|
|
Note F- Phenolic impregnated resin, K-Furan resin, D-Antimony ( please refer to technical data for specific’s£©
|